Influence of surface texture and acid-base properties on ozone decomposition catalyzed by aluminium (hydroxyl) oxides

Abstract

The decomposition of aqueous ozone in the presence of three aluminum (hydroxyl) oxides was studied,respectively. It was hypothesized that surface hydroxyl groups and acid-base properties of aluminum(hydroxyl) oxides play an important role in catalyzed ozone decomposition. The variables investigatedwere oxide dose, aqueous pH, presence of inorganic anions (sulfate and nitrate), the effect of tert-butylalcohol (TBA) and surface hydroxyl groups density of the three aluminum (hydroxyl) oxides. All threealuminum (hydroxyl) oxides tested, i.e. g-AlOOH (HAO), g-Al2O3 (RAO) and a-Al2O3 (AAO), enhanced the rate of ozone decomposition. The net surface charge of the aluminum (hydroxyl) oxides favored incatalyzed ozone decomposition. The greatest effect on catalyzed ozone decomposition was observedwhen the solution pH was close to the point of zero charge of the aluminum (hydroxyl) oxide. Sulfate and nitrate were substituted for the surface hydroxyl groups of the aluminum (hydroxyl) oxides, which then complexed with Al3+ in a ligand exchange reaction. Therefore, inorganic anions may be able to inhibit catalyzed ozone decomposition. It was confirmed that surface hydroxyl groups were important for ozone decomposition with aluminum (hydroxyl) oxides as catalysts. TBA inhibited ozone decomposition in the presence of HAO, RAO and AAO. It was also tested whether aluminum (hydroxyl) oxides catalyzed ozonetransformed hydroxyl radicals. The relationship between surface hydroxyl groups and the ratio of hydroxyl radical concentration to ozone concentration (Rct) was investigated quantitatively. Higher density of surface hydroxyl groups of the aluminum oxide tested was favorable for the decay of ozone into hydroxyl radicals.